Highly micronized particle size for exceptional dispersion and surface uniformity.
Polar modification enhances compatibility with polar resins, pigments, and additives.
Excellent matting and slip performance without compromising gloss control.
Thermally stable up to 140 °C, supporting high-temperature processing in extrusion and compounding.
Low volatility and minimal plate-out tendency during continuous operation.
Engineering thermoplastics (e.g., PA6, PA66, PBT) for internal lubrication and mold release.
Color masterbatches to improve pigment dispersion and reduce agglomeration.
Wood-plastic composites (WPC) for surface finish enhancement and extruder die lubrication.
Thermoplastic elastomers (TPE) requiring balanced melt flow and surface aesthetics.
| Chemical Type | Polar-modified low-density polyethylene wax |
| Product Form | Free-flowing white powder |
| Appearance | White to off-white micro-powder |
| Median Particle Size (D50) | ≈ 5–7 µm |
| Melting Point (DSC, 10 °C/min) | 108–112 °C |
| Acid Number | 12–16 mg KOH/g |
| Bulk Density | 350–420 g/L |
| Key Features | Improved polarity, micronized morphology, low plate-out |