Highly uniform metallocene-catalyzed polyethylene backbone ensures narrow molecular weight distribution and exceptional batch-to-batch consistency.
Controlled maleic anhydride grafting provides strong polar functionality for enhanced adhesion to inorganic fillers, metals, and polar polymers.
Low melt viscosity enables excellent processability in extrusion, compounding, and dispersion applications without thermal degradation.
Outstanding thermal stability up to 280 °C supports high-temperature processing in engineering thermoplastics and masterbatch production.
Non-toxic, REACH-compliant formulation suitable for demanding applications including food-contact-adjacent compounds (subject to final formulation approval).
Compatibilizer in polyolefin-based composites with calcium carbonate, talc, or glass fiber.
Dispersing aid for pigment and additive masterbatches in PP, PE, and TPO systems.
Adhesion promoter in multi-layer coextruded films and metal/polymer laminates.
Processing aid and surface modifier in wood-plastic composites (WPC) and mineral-filled PVC profiles.
Functional wax component in hot-melt adhesives requiring improved substrate wetting and cohesion.
| Chemical Type | Maleic anhydride grafted metallocene polyethylene wax |
| Product Form | Pellets |
| Appearance | White to off-white free-flowing pellets |
| Melt Point (°C, DSC, 10 °C/min) | 108–114 |
| MAH Content (wt%, titration) | 3.8–4.4 |
| Melt Flow Rate (g/10 min, 190 °C/2.16 kg) | 25–35 |
| Density (g/cm³, 23 °C) | 0.915–0.925 |
| Key Features | High polarity, low volatility, excellent thermal stability, metallocene-derived narrow MWD |