Low-viscosity, trifunctional propylene oxide–initiated polyether polyol for improved processability.
Consistent hydroxyl value (OHV) and narrow molecular weight distribution ensure reliable reactivity in polyurethane systems.
Excellent compatibility with aromatic and aliphatic isocyanates, supporting stable foam and elastomer formation.
Low residual monomer and catalyst content meet stringent industrial safety and emission requirements.
Stable storage performance with minimal color development over time under recommended conditions.
Flexible slabstock polyurethane foams for bedding and upholstered furniture.
Integral skin foams used in automotive interior components (e.g., armrests, headrests).
Microcellular elastomers for gasketing, seals, and vibration-damping parts.
Rigid insulation foams in cold-chain packaging and refrigeration panels.
Coating and adhesive formulations requiring balanced flexibility and chemical resistance.
| Chemical Type | Trifunctional propylene oxide–based polyether polyol |
| Product Form | Liquid |
| Appearance | Clear, pale yellow liquid |
| Hydroxyl Value (mg KOH/g) | 300–310 |
| Viscosity at 25°C (mPa·s) | 280–360 |
| Water Content (wt%) | ≤ 0.05 |
| pH (10% aqueous solution) | 5.5–7.0 |
| Primary Applications | Flexible & semi-rigid PU foams, elastomers, coatings |