Low-viscosity, high-molecular-weight polyethylene wax offering excellent melt flow and processability in high-speed compounding.
Superior lubricity and mold release performance, reducing friction and improving surface finish in thermoplastic formulations.
High thermal stability up to 250 °C, enabling compatibility with engineering resins processed at elevated temperatures.
Excellent dispersion stability in both polar and non-polar polymer matrices, minimizing agglomeration during extrusion.
Consistent batch-to-batch quality with narrow molecular weight distribution (Mw/Mn ≈ 12–15), ensuring predictable rheological behavior.
Internal and external lubricant in PVC compounds for rigid profiles, flooring, and cable sheathing.
Processing aid in engineering thermoplastics including PA6, PBT, and PC blends.
Slip and anti-blocking agent in masterbatches for polyolefin films and injection-molded parts.
Surface modifier in pigment concentrates to enhance wetting, dispersion, and color development.
Release agent in rubber compound processing and thermoset composites manufacturing.
| Chemical Type | High-density polyethylene (HDPE) homopolymer wax |
| Product Form | Pellets (cylindrical, ~3 mm diameter) |
| Appearance | White to off-white semi-crystalline solid |
| Melt Point (DSC, °C) | 128–132 |
| Penetration (25 °C, 0.1 mm, ASTM D1321) | 4–7 |
| Viscosity (150 °C, mPa·s, Brookfield CAP2000+) | 180–220 |
| Density (g/cm³, 23 °C) | 0.935–0.945 |
| Volatile Content (wt%, 120 °C/2 h) | < 0.3 |