High hydrophobicity with excellent water repellency for long-term protection against moisture ingress.
Low-VOC formulation compliant with stringent environmental regulations and indoor air quality standards.
Outstanding adhesion to diverse mineral substrates including concrete, mortar, and masonry.
Good film-forming capability at low temperatures (down to 5 °C), enabling extended application windows.
Enhanced alkali resistance suitable for use in cementitious systems without film degradation.
Waterproofing slurries for below-grade concrete structures and foundations.
Flexible cementitious waterproofing membranes for balconies, terraces, and wet areas.
Admixture in polymer-modified tile adhesives and grouts requiring enhanced water resistance.
Base component in breathable exterior renders and façade protection systems.
Modification agent for repair mortars exposed to intermittent water contact.
| Chemical Type | Aqueous acrylic copolymer emulsion |
| Product Form | Liquid, ready-to-use dispersion |
| Appearance | White to slightly bluish opaque liquid |
| pH (at 23 °C) | 7.5 – 8.5 |
| Solids Content (wt %) | 48.0 – 50.0 |
| Minimum Film Formation Temperature (MFFT) | ≈ 5 °C |
| Viscosity (Brookfield RVT, spindle 3, 20 rpm, 23 °C) | 1,500 – 3,500 mPa·s |
| VOC Content | < 50 g/L (EN ISO 11890-2) |