Excellent water resistance and chemical stability in aqueous formulations.
Superior adhesion to diverse substrates including metals, plastics, and concrete.
Low film-forming temperature (MFT) enabling efficient ambient-cure applications.
Good mechanical strength and flexibility after film formation.
Compatible with common additives such as pigments, fillers, and coalescing agents.
Water-based industrial coatings for metal protection.
High-performance primers and undercoats for automotive and appliance finishes.
Corrosion-inhibiting coatings for steel structures and pipelines.
Adhesive binders in nonwoven fabric and specialty paper manufacturing.
Functional coatings for building materials requiring weather resistance and durability.
| Chemical Type | Vinyl chloride–vinyl acetate copolymer emulsion |
| Product Form | Aqueous emulsion |
| Appearance | White to off-white opaque liquid |
| Solids Content | 60 ± 1 wt% |
| pH | 1.5 – 2.5 |
| Viscosity (25°C, Brookfield RVT, #3 spindle, 20 rpm) | 100 – 300 mPa·s |
| Minimum Film Formation Temperature (MFT) | ≈ 10°C |
| Particle Size (D50) | 0.2 – 0.4 µm |