Excellent chemical resistance to acids, alkalis, and aliphatic hydrocarbons.
Superior adhesion to diverse substrates including metal, concrete, and PVC.
Good film-forming capability with balanced flexibility and hardness after drying.
Low volatile organic compound (VOC) content, supporting environmentally compliant formulations.
Stable emulsion with consistent viscosity and long shelf life under recommended storage conditions.
Water-based industrial coatings for corrosion protection of steel structures.
High-performance linings for tanks, pipes, and chemical containment systems.
Binders in specialty mortars and repair compounds for concrete rehabilitation.
Base resin in flame-retardant and low-smoke cable jacketing compounds.
Component in flexible, waterproof membranes for roofing and waterproofing applications.
| Chemical Type | Vinyl chloride–vinyl acetate copolymer emulsion |
| Product Form | Aqueous emulsion |
| Appearance | White to off-white opaque liquid |
| Solids Content | 47–49 wt% |
| pH | 6.5–7.5 |
| Viscosity (Brookfield, LVT, #3 spindle, 20 rpm, 25°C) | 100–300 mPa·s |
| Minimum Film Formation Temperature (MFFT) | 12–15°C |
| Storage Stability | Stable for ≥6 months at 5–30°C; no coagulum or phase separation |