Highly optimized for excellent open time and workability in tile adhesives and cementitious renders.
Provides superior green strength development and early adhesion to low-absorbent substrates such as porcelain tiles and concrete.
Enhances flexibility and crack bridging capacity without compromising cement compatibility.
Low residual monomer content ensures compliance with stringent VOC and safety regulations.
Consistent batch-to-batch performance due to controlled polymerization and rigorous quality control.
Cement-based tile adhesives (C1 and C2 classifications per EN 12004).
Exterior thermal insulation composite systems (ETICS) base coats and finishing renders.
Repair mortars and self-leveling underlayments requiring enhanced cohesion and substrate bonding.
Waterproofing slurries and flexible cementitious coatings for wet-area applications.
Grouts and joint fillers where improved deformability and reduced shrinkage are critical.
| Chemical Type | Polyvinyl acetate (PVAc) homopolymer dispersion |
| Product Form | Aqueous dispersion (non-ionic stabilizer system) |
| Appearance | White, slightly opalescent liquid |
| Solids Content | Approx. 55 wt.% |
| pH Value | 4.5–5.5 |
| Viscosity (20 °C, Brookfield RVT, spindle 3, 2 rpm) | 1,500–3,500 mPa·s |
| Minimum Film Formation Temperature (MFFT) | ≈ 15 °C |
| Residual Vinyl Acetate Monomer | < 100 ppm |