High solids content for efficient formulation and reduced drying time.
Excellent adhesion to porous substrates such as concrete, plaster, and gypsum board.
Good film-forming properties with balanced flexibility and hardness after drying.
Low minimum film formation temperature (MFFT) enabling use in ambient curing conditions.
Compatible with common inorganic fillers and cement-based systems without destabilization.
Tile adhesives for ceramic and porcelain tiles on interior walls and floors.
Repair mortars and patching compounds for concrete and masonry substrates.
Self-leveling underlayments and floor screeds requiring enhanced workability and bond strength.
Exterior insulation finishing systems (EIFS) base coats and reinforcing layers.
Water-resistant plasters and renders for façade applications.
| Chemical Type | Polyvinyl acetate (PVA) homopolymer dispersion |
| Product Form | Aqueous dispersion |
| Appearance | White to slightly yellowish, milky liquid |
| Solids Content | Approx. 54–56 wt.% |
| pH Value | 4.5–5.5 |
| Viscosity (at 20 °C) | 150–350 mPa·s (Brookfield RVD, spindle #3, 12 rpm) |
| Minimum Film Formation Temperature (MFFT) | Approx. 12–14 °C |
| Storage Stability | At least 6 months at 5–30 °C in original sealed container |