High solids content (≈50%) enabling efficient formulation with reduced water usage.
Excellent adhesion to porous and non-porous substrates including concrete, plaster, and wood.
Good film-forming capability at ambient temperatures without coalescing agents.
Low minimum film formation temperature (MFFT ≈ 10 °C) supporting reliable performance in moderate climates.
Stable viscosity profile over time, ensuring consistent processing in industrial mixing systems.
Cementitious tile adhesives for interior and exterior ceramic and stone installations.
Reinforced plaster and render formulations to enhance crack resistance and workability.
Repair mortars and grouts requiring improved flexibility and bond strength.
Self-leveling underlayments for improved flow and substrate adhesion.
Waterproofing slurries and primers for masonry and concrete surfaces.
| Chemical Type | Polyvinyl acetate (PVAc) homopolymer dispersion |
| Product Form | Aqueous dispersion |
| Appearance | White, slightly opalescent liquid |
| Solids Content | 49–51 wt.% |
| pH Value | 4.5–5.5 |
| Viscosity (20 °C, Brookfield RVT, spindle #3, 20 rpm) | 150–350 mPa·s |
| Minimum Film Formation Temperature (MFFT) | ≈10 °C |
| Storage Stability | ≥6 months at 5–30 °C (unopened container) |