High molecular weight polyvinyl acetate resin offering excellent film-forming capability and cohesive strength.
Optimized for water-based formulations with good colloidal stability and low foaming tendency.
Provides outstanding adhesion to porous substrates such as wood, paper, and concrete.
Delivers balanced flexibility and hardness in dried films, minimizing cracking under thermal cycling.
Free of added formaldehyde and compliant with stringent VOC regulations for industrial coatings and adhesives.
Interior wall paints and decorative coatings requiring scrub resistance and low-odor performance.
High-solids, low-VOC wood adhesives for laminated flooring and furniture assembly.
Reinforcing binder in dry-mix mortars for tile adhesives and repair plasters.
Key binder in non-woven fabric impregnation for technical textiles and filtration media.
Stabilizing polymer in cementitious grouts and self-leveling compounds.
| Chemical Type | Polyvinyl acetate (PVA) homopolymer |
| Product Form | Aqueous dispersion (65 wt% solids) |
| Appearance | White to slightly yellowish opaque liquid |
| pH (25 °C) | 4.5 – 5.5 |
| Viscosity (Brookfield RVT, 20 rpm, 23 °C) | 1,200 – 2,500 mPa·s |
| Minimum Film Formation Temperature (MFFT) | ~18 °C |
| Residual Vinyl Acetate Monomer | < 50 ppm |
| Storage Stability (at 5–30 °C) | ≥ 6 months without sedimentation or coagulation |