High molecular weight polyvinyl acetate copolymer offering excellent film-forming properties and cohesive strength.
Optimized for low-temperature flexibility and improved adhesion on porous substrates such as wood, concrete, and gypsum board.
Low residual monomer content (< 100 ppm vinyl acetate), supporting compliance with stringent environmental and safety standards.
Good hydrolytic stability and resistance to alkaline conditions commonly encountered in cementitious systems.
Designed for easy integration into water-based formulations without requiring organic solvents or plasticizers.
Tile adhesives and thin-set mortars for interior and exterior ceramic and natural stone installations.
Repair mortars and self-leveling underlayments requiring enhanced workability and bond strength.
Exterior insulation finishing systems (EIFS) base coats and reinforcing layers.
Waterproofing slurries and flexible cementitious coatings for balconies and wet areas.
Grouts and joint fillers where crack-bridging capability and long-term durability are critical.
| Chemical Type | Partially hydrolyzed polyvinyl acetate copolymer |
| Product Form | Aqueous dispersion (latex) |
| Appearance | White to slightly yellowish opaque liquid |
| Solids Content | 54–56 wt % |
| pH Value | 4.5–5.5 |
| Viscosity (at 20 °C, Brookfield RVT, spindle #3, 20 rpm) | 1,500–3,000 mPa·s |
| Minimum Film Formation Temperature (MFFT) | ≈ 10 °C |
| Residual Vinyl Acetate Monomer | < 100 ppm |