Kraton D-1401P Impact Modifier

Kraton D-1401P is a high-performance linear SBS block copolymer with excellent flexural and tensile properties. It can modify with resins and rubbers, adjust material viscosity and hardness, suitable for multiple processing technologies.

Features Of Kraton D-1401P Impact Modifier

  1. Excellent mechanical properties, high flexural strength and modulus, strong structural stability.

  2. Good compatibility with resins and rubbers, optimizing substrate comprehensive performance.

  3. Wide processing adaptability, compatible with injection molding, extrusion and other processes.

  4. Adjustable material viscosity and hardness to meet diverse product requirements.

  5. Superior flex resistance, enhancing product durability and service life.

Typical Applications Of Kraton D-1401P Impact Modifier

  1. Asphalt modification: Applied in road paving and waterproof membranes to improve weather resistance and crack resistance.

  2. Shoe material manufacturing: Produce shoe soles and edges for good elasticity and wear resistance.

  3. Adhesives: Make hot melt and pressure-sensitive adhesives to enhance flexibility and bonding strength.

  4. Auto parts: Fabricate seals and shock pads for complex working conditions in vehicles.

  5. Elastic products: Process pipes and sheets to meet daily and industrial application needs.

Specifications Of Kraton D-1401P Impact Modifier


Melt Flow Rate11 g/10min (ASTM D-1238)
Specific Gravity1.01 g/cm³ (ASTM D-792)
Flexural Strength37.2 MPa (ASTM D-790)
Flexural Modulus1720 MPa (ASTM D-790)
Tensile Strength24.8 MPa (ASTM D-638)
Elongation at Break200% (ASTM D-638)
Hardness (Shore A)85 (ASTM D2240)
Vicat Softening Temperature95℃ (ASTM D1525)
Compression Set28% (22h, 70℃) (ASTM D395)