Kraton D-1403P is a high-performance linear SBS block copolymer with excellent flexural and tensile properties. It modifies with resins/rubbers, adjusts viscosity and hardness, features low shrinkage for diverse processing.
Excellent mechanical properties, high flexural strength and modulus, strong structural stability.
Good compatibility with resins and rubbers, optimizing substrate comprehensive performance.
Low molding shrinkage, high product dimensional accuracy for precision processing.
Wide processing adaptability, compatible with injection molding, extrusion and other processes.
Superior flex resistance, enhancing product durability and service life.
Asphalt modification: Applied in road paving and waterproof membranes to improve weather and crack resistance.
Shoe material manufacturing: Produce shoe soles and edges for good elasticity and wear resistance.
Adhesives: Make hot melt and pressure-sensitive adhesives to enhance flexibility and bonding strength.
Auto parts: Fabricate seals and shock pads for complex working conditions in vehicles.
Elastic products: Process pipes and sheets to meet daily and industrial application needs.
| Melt Flow Rate | 11 g/10min (ASTM D-1238) |
| Specific Gravity | 1.01 g/cm³ (ASTM D-792) |
| Flexural Strength | 40.1 MPa (ASTM D-790) |
| Flexural Modulus | 1830 MPa (ASTM D-790) |
| Tensile Strength | 27.4 MPa (ASTM D-638) |
| Molding Shrinkage | 0.4% (ASTM D-955) |
| Elongation at Break | 200% (ASTM D-638) |
| Hardness (Shore A) | 88 (ASTM D2240) |
| Vicat Softening Temperature | 98℃ (ASTM D1525) |
| Compression Set | 25% (22h, 70℃) (ASTM D395) |