Enhances melt flow and processability in high-viscosity thermoplastics without compromising mechanical properties.
Reduces extrusion torque and die swell, enabling stable high-output operation in twin-screw extruders.
Improves pigment dispersion and surface gloss in colored compounds, especially for engineering resins.
Thermally stable up to 300 °C, suitable for processing polyamides, PBT, and other high-melting engineering polymers.
Low volatility and non-migrating — minimizes plate-out and maintains long-term die cleanliness.
Engineering thermoplastics compounding (e.g., PA6, PA66, PBT).
Color masterbatch production for automotive and appliance applications.
Recycled polymer reprocessing to restore melt homogeneity and reduce filter pressure buildup.
High-performance cable jacketing compounds requiring consistent extrusion and surface finish.
Conductive and flame-retardant compound lines where additive compatibility and dispersion stability are critical.
| Chemical Type | Ester-modified polyolefin wax blend |
| Product Form | Pellets |
| Appearance | Off-white to light yellow free-flowing pellets |
| Density (23 °C) | ~0.92–0.94 g/cm³ |
| Melt Point (DSC, 10 °C/min) | 115–125 °C |
| Softening Point (Ring & Ball) | 110–118 °C |
| Volatile Content (105 °C, 2 h) | < 0.5 wt% |
| Primary Applications | Processing aid for engineering thermoplastics and masterbatches |