Excellent chemical resistance, particularly to acids, alkalis, and aliphatic hydrocarbons.
Superior film-forming capability with good flexibility and adhesion on diverse substrates including metal, concrete, and plastics.
Low VOC content and APEO-free formulation, supporting compliance with stringent environmental and regulatory standards.
Stable emulsion with high mechanical and freeze-thaw stability, ensuring consistent performance during storage and handling.
Optimized particle size distribution for smooth coating application and uniform film appearance.
Industrial protective coatings for steel structures and process equipment.
Waterproofing membranes and tank linings in chemical storage and wastewater treatment facilities.
Corrosion-inhibiting primers for marine and offshore infrastructure.
High-performance topcoats for pre-fabricated building panels and architectural cladding systems.
Binders in specialty construction mortars and polymer-modified cementitious coatings.
| Chemical Type | Vinyl chloride–vinyl acetate–maleic anhydride terpolymer emulsion |
| Product Form | Aqueous emulsion |
| Appearance | White to off-white, homogeneous liquid |
| Solids Content (wt%) | 58.0 ± 1.0 |
| pH (at 25°C) | 3.5 – 4.5 |
| Viscosity (mPa·s, Brookfield RVT, #2 spindle, 20 rpm) | 100 – 300 |
| Minimum Film Formation Temperature (MFFT) | ≈ 15°C |
| Free Vinyl Chloride Monomer (VCM) Content | < 1 ppm |