High-performance two-component epoxy system with excellent peel and shear strength.
Designed for structural bonding of composites, metals, and thermoset substrates.
Low-viscosity formulation enables precise dispensing and superior gap-filling capability.
Room-temperature cure option with accelerated cure at elevated temperatures (e.g., 60–80 °C).
Outstanding resistance to thermal cycling, humidity, and aerospace-grade environmental aging.
Aerospace interior components bonding (e.g., panels, trim, brackets).
Structural assembly of carbon fiber reinforced polymer (CFRP) parts.
Bonding of aluminum and titanium structures in transport and defense systems.
Joining of honeycomb core sandwich panels for lightweight airframe applications.
Repair and rework of composite tooling and molds in manufacturing environments.
| Chemical Type | Two-part aromatic amine-cured epoxy resin system |
| Product Form | Two-component paste (Part A: resin, Part B: hardener) |
| Appearance | Off-white to light tan viscous paste (Part A); pale amber paste (Part B) |
| Mix Ratio by Weight | 100 : 35 (A : B) |
| Working Life (23 °C) | ≥ 90 minutes after mixing |
| Full Cure Condition | 24 hours at 23 °C or 2 hours at 80 °C |
| Primary Applications | Structural bonding in aerospace, defense, and high-performance transport |
| Key Features | Low volatile content, non-halogenated, qualified per Boeing BSS 7239 and Airbus AIMS01-06-002 |