High solids content for improved film formation and reduced drying time.
Excellent adhesion to diverse substrates including concrete, plaster, and wood.
Outstanding freeze-thaw stability (tested over 5 cycles at −5 °C).
Low residual monomer content meeting stringent VOC and regulatory requirements.
Good mechanical strength and flexibility in cured films, even at low temperatures.
Cementitious tile adhesives and grouts.
Exterior insulation finishing systems (EIFS) base coats.
Repair mortars and polymer-modified renders.
Self-leveling underlayments and flooring compounds.
Waterproofing membranes for concrete substrates.
| Chemical Type | VAE (Vinyl Acetate-Ethylene) Copolymer Emulsion |
| Product Form | Aqueous emulsion |
| Appearance | White to slightly yellowish, homogeneous liquid |
| Solids Content (wt. %) | 58.0 ± 0.5 |
| pH (at 20 °C) | 4.5 – 5.5 |
| Viscosity (mPa·s, Brookfield RVT, spindle 3, 2 rpm) | 150 – 350 |
| Minimum Film Formation Temperature (MFFT) | ≈ 10 °C |
| Residual Vinyl Acetate (mg/kg) | < 100 |