Excellent adhesion to diverse substrates including concrete, plaster, and aged paints.
Outstanding freeze-thaw stability (tested over 5 cycles at −4 °C).
Low residual monomer content, meeting stringent VOC and regulatory requirements.
Good mechanical resistance and flexibility after film formation.
Cementitious tile adhesives and grouts.
Exterior insulation finishing systems (EIFS) base coats.
Repair mortars and polymer-modified rendering plasters.
Self-leveling underlayments and floor screeds.
Waterproofing slurries for concrete structures.
| Chemical Type | VAE (Vinyl Acetate-Ethylene) copolymer emulsion |
| Product Form | Aqueous dispersion |
| Appearance | White, slightly opalescent liquid |
| Solids Content | 60.0 ± 1.0 wt % |
| pH Value | 4.5 – 5.5 |
| Minimum Film Formation Temperature (MFFT) | ≈ 12 °C |
| Viscosity (at 20 °C, Brookfield RVT, spindle 3, 20 rpm) | 150 – 400 mPa·s |
| Residual Vinyl Acetate Monomer | < 0.02 wt % |