High-performance vinyl acetate–ethylene (VAE) copolymer emulsion with excellent film-forming capability at ambient temperatures.
Outstanding adhesion to diverse substrates including concrete, plaster, wood, and aged paints without primer.
Low minimum film formation temperature (MFFT) of approximately 10 °C, enabling reliable performance in moderate climates.
Good hydrophobicity and water resistance after film coalescence, enhancing durability in humid environments.
Low volatile organic compound (VOC) content, compliant with stringent environmental and occupational safety regulations.
Cementitious tile adhesives for interior and exterior ceramic, porcelain, and natural stone installations.
Flexible waterproofing membranes for balconies, terraces, and wet-area construction.
Reinforced repair mortars and polymer-modified rendering systems for façade restoration.
Self-leveling underlayments requiring enhanced cohesion, flexibility, and substrate bonding.
| Chemical Type | VAE (Vinyl Acetate–Ethylene) Copolymer Emulsion |
| Product Form | White, milky liquid emulsion |
| Appearance | Homogeneous, slightly opalescent dispersion |
| Solids Content (wt %) | 59–61 % |
| pH Value (at 23 °C) | 4.5–5.5 |
| Viscosity (mPa·s, Brookfield RVT, spindle 3, 20 rpm) | 50–150 |
| Minimum Film Formation Temperature (MFFT) | ≈10 °C |
| VOC Content | <50 g/L |