High solids content for improved film formation and reduced drying time.
Excellent adhesion to porous and non-porous substrates including concrete, plaster, and wood.
Good freeze-thaw stability (3 cycles at –4 °C / +23 °C) ensuring reliable storage and handling.
Low minimum film formation temperature (MFFT) of approximately 12 °C for consistent performance in moderate climates.
Low residual monomer content (< 0.05 wt-% vinyl acetate), supporting safe formulation and regulatory compliance.
Tile adhesives for interior and exterior ceramic and porcelain tile installations.
Cementitious repair mortars and leveling compounds requiring enhanced flexibility and bond strength.
Exterior insulation finishing systems (EIFS) base coats and reinforcement layers.
Waterproofing membranes and flexible cement-based coatings.
Self-leveling underlayments with improved workability and crack bridging capability.
| Chemical Type | VAE (Vinyl Acetate-Ethylene) copolymer emulsion |
| Product Form | Aqueous polymer dispersion |
| Appearance | White to slightly yellow, milky liquid |
| Solids Content | 69–71 wt-% |
| pH Value | 4.5–5.5 |
| Viscosity (20 °C, Brookfield RVT, spindle 3, 2 rpm) | 1,500–3,500 mPa·s |
| Residual Vinyl Acetate | < 0.05 wt-% |
| Minimum Film Formation Temperature (MFFT) | ≈ 12 °C |