Excellent adhesion to non-porous substrates including concrete, ceramic tiles, and metal.
High flexibility and crack-bridging capability for durable performance in dynamic joints.
Low minimum film formation temperature (MFFT) enabling reliable film formation at ambient conditions.
Good water resistance after film formation, supporting long-term durability in humid environments.
Compatible with common construction additives such as cellulose ethers, redispersible powders, and defoamers.
Cementitious tile adhesives (C2 and C2TES1 according to EN 12004).
Flexible waterproofing membranes for balconies, terraces, and wet areas.
Repair mortars requiring high bond strength and deformation tolerance.
Self-leveling underlayments with enhanced flow and substrate adhesion.
Exterior insulation finishing systems (EIFS) base coats for improved impact resistance.
| Chemical Type | VAE (Vinyl Acetate-Ethylene) copolymer emulsion |
| Product Form | Aqueous polymer emulsion |
| Appearance | White, slightly opalescent liquid |
| Solids Content | 59–61 wt % |
| pH Value | 4.5–5.5 |
| Viscosity (at 23 °C) | 50–150 mPa·s (Brookfield RVT, spindle #3, 20 rpm) |
| Minimum Film Formation Temperature (MFFT) | ≈ 12 °C |
| Storage Stability | Stable for ≥ 6 months at 5–30 °C in sealed original container |