High-performance vinyl acetate–ethylene (VAE) copolymer emulsion with excellent film-forming capability at ambient temperatures.
Outstanding adhesion to diverse substrates including concrete, plaster, wood, and aged paints.
Enhanced water resistance and scrub resistance in cured films without requiring external crosslinkers.
Low minimum film formation temperature (MFFT) of approximately 12 °C, enabling reliable performance in moderate climates.
Good compatibility with common construction additives such as cellulose ethers, defoamers, and pigments.
Interior and exterior architectural coatings for premium-quality wall paints and primers.
Tile adhesives and thin-set mortars requiring high green strength and extended open time.
Repair mortars and polymer-modified cementitious renders for façade restoration.
Decorative plasters and textured finishes demanding crack bridging and flexibility.
Waterproofing slurries and protective coatings for concrete substrates.
| Chemical Type | VAE (Vinyl Acetate–Ethylene) Copolymer Emulsion |
| Product Form | Aqueous polymer emulsion |
| Appearance | White to slightly bluish, opaque liquid |
| Solids Content (wt. %) | 55.0 ± 1.0 |
| pH (at 23 °C) | 4.5 – 5.5 |
| Viscosity (mPa·s, Brookfield RVT, spindle 3, 20 rpm) | 500 – 1500 |
| Minimum Film Formation Temperature (MFFT) | ≈ 12 °C |
| Residual Vinyl Acetate Monomer (VAM) | < 100 ppm |