Excellent balance of mechanical strength and impact resistance for structural composite parts.
Low viscosity (250–350 cP at 25°C) enabling superior fiber wet-out and efficient resin transfer molding (RTM) processing.
Good heat distortion temperature (HDT ≈ 85–90°C) after post-curing, supporting mid-temperature service applications.
Consistent reactivity profile with standard MEKP initiators, ensuring reliable gel time control in ambient and warm-cure operations.
High solids content (>99%) with low styrene emission potential, contributing to improved workplace safety and VOC compliance.
Fiberglass-reinforced plastic (FRP) tanks and chemical storage vessels.
Automotive body panels and under-hood components requiring dimensional stability and surface finish.
Marine deck structures, hull liners, and recreational boat components.
Industrial grating, cable trays, and corrosion-resistant ductwork.
Pultruded profiles for construction reinforcement and infrastructure applications.
| Chemical Type | Orthophthalic unsaturated polyester resin |
| Product Form | Liquid, ready-to-use |
| Appearance | Clear to pale yellow, homogeneous liquid |
| Viscosity (25°C) | 250–350 cP |
| Gel Time (with 1.0% MEKP, 25°C) | 12–18 minutes |
| Reactive Diluent | Styrene (35–40% w/w) |
| Solids Content | ≥99% |
| Density (25°C) | 1.11–1.13 g/cm³ |