Waterborne formulation with zero VOC emissions, compliant with stringent environmental regulations including EU REACH and US EPA standards.
Excellent initial tack and rapid green strength development for high-speed industrial lamination processes.
Superior heat resistance up to 80°C after full cure, maintaining bond integrity under thermal stress.
Outstanding flexibility and elongation (>300%), ideal for bonding substrates with differential thermal expansion.
Good resistance to moisture, plasticizers, and mild alkaline cleaners post-cure.
Automotive interior trim lamination (e.g., PVC/TPU to ABS, PP, or composite substrates).
Flexible packaging lamination for food-grade pouches and medical blister packaging.
Technical textile bonding, including laminated membranes for outdoor apparel and protective workwear.
Wood-based panel lamination (MDF, particleboard) with decorative HPL or veneer overlays.
Industrial label facestock-to-liner bonding requiring high shear resistance and low migration.
| Chemical Type | Aliphatic waterborne polyurethane dispersion (anionic) |
| Product Form | Opaque white liquid, ready-to-use |
| Appearance | Homogeneous milky dispersion, no sedimentation |
| pH (25°C) | 7.8 – 8.4 |
| Solids Content (wt%) | 38.0 ± 1.0% |
| Viscosity (mPa·s, Brookfield RVT, #3 spindle, 20 rpm, 25°C) | 3,500 – 5,500 |
| Minimum Film Formation Temperature (MFFT) | ≥ 15°C |
| Storage Stability (unopened, 5–30°C) | ≥ 6 months |