Two-component, room-temperature curing epoxy system with excellent adhesion to metals, composites, and thermosets.
High shear and peel strength retention after thermal aging up to 120 °C and exposure to humidity.
Low volatile organic compound (VOC) content, supporting industrial compliance with environmental and workplace safety standards.
Controlled pot life of approximately 60–90 minutes at 23 °C, enabling consistent manual or automated dispensing.
Non-sag formulation suitable for vertical and overhead bonding without slumping or migration.
Aerospace structural bonding of aluminum, titanium, and carbon fiber reinforced polymer (CFRP) components.
Automotive powertrain assembly, including sensor mounting and heat shield attachment.
Electronics encapsulation and thermal interface bonding in high-reliability industrial control units.
Railway vehicle interior panel lamination and metal-to-composite fastening under vibration and thermal cycling conditions.
| Chemical Type | Bisphenol-A based epoxy resin system with amine hardener |
| Product Form | Two-component liquid (Part A: resin; Part B: hardener) |
| Appearance (Mixed) | Homogeneous, amber-colored viscous liquid |
| Mix Ratio by Weight | 100 : 35 (Part A : Part B) |
| Cure Schedule (Standard) | 24 hours at 23 °C, or accelerated cure at 80 °C for 2 hours |
| Density (Mixed, 23 °C) | Approx. 1.25 g/cm³ |
| Primary Applications | Structural bonding, metal-to-composite joining, and high-durability industrial assembly |
| Key Features | Room-temperature cure, low VOC, non-sag, thermal stability, and robust moisture resistance |