Two-component, room-temperature curing epoxy adhesive system with excellent toughness and peel resistance.
Outstanding adhesion to composites, aluminum, titanium, stainless steel, and thermoset substrates without extensive surface pretreatment.
Low volatile organic compound (VOC) content, compliant with stringent aerospace and industrial environmental requirements.
Long working life (pot life) of up to 120 minutes at 23 °C, enabling complex assembly operations.
Qualified to major aerospace specifications including BMS 8-276, Airbus ABR 4000, and Boeing D6-17487 Rev. T.
Aerospace structural bonding: wing skins, fuselage panels, and empennage assemblies.
Repair of carbon fiber reinforced polymer (CFRP) components in commercial and military aircraft.
Bonding of honeycomb core sandwich structures in radomes and interior panels.
Joining of dissimilar metals in high-reliability defense and space platforms.
Secondary bonding of thermoset composite parts during aircraft final assembly.
| Chemical Type | Epoxy resin / amine hardener system |
| Product Form | Two-component paste (Part A: resin, Part B: hardener) |
| Appearance | Off-white to light tan paste (Part A), pale yellow paste (Part B) |
| Mix Ratio (by weight) | 100 : 35 (A:B) |
| Cure Schedule (standard) | 23 °C for 7 days or 60 °C for 2 hours |
| Density (23 °C) | ~1.35 g/cm³ (mixed) |
| Storage Life | 12 months at ≤25 °C (unopened) |
| Primary Applications | Structural bonding in aerospace and defense composites and metals |