Highly flexible and impact-resistant due to proprietary polyether-modified backbone.
Excellent adhesion to low-surface-energy substrates including polyolefins and treated metals.
Reduced viscosity versus standard bisphenol-A epoxies, enabling easier processing and improved filler wetting.
Good chemical resistance to alcohols, weak acids, and alkaline cleaners after full cure.
Compatible with conventional amine and anhydride curing agents for tailored thermal and mechanical profiles.
Structural adhesives for automotive bonding (e.g., metal-to-composite, battery module assembly).
Encapsulants and potting compounds for electronics requiring thermal cycling durability.
High-performance coatings for industrial flooring and corrosion-resistant linings.
Composite matrix resins in wind turbine blade root joints and aerospace secondary structures.
| Chemical Type | Polyether-modified liquid epoxy resin |
| Product Form | Clear to pale yellow viscous liquid |
| Appearance | Homogeneous, slightly hazy liquid at room temperature |
| Epoxy Equivalent Weight (EEW) | 390–410 g/eq |
| Viscosity (25°C) | 8,000–12,000 mPa·s |
| Density (25°C) | 1.12–1.15 g/cm³ |
| Primary Applications | Adhesives, encapsulants, coatings, composite matrices |
| Key Features | Flexibility, adhesion, processability, chemical resistance |