Low VOC content (< 50 g/L), compliant with stringent global environmental regulations including EU REACH and US EPA standards.
Excellent film-forming capability at room temperature, yielding flexible, transparent, and abrasion-resistant coatings.
Outstanding hydrolytic stability and storage stability (≥12 months at 5–35°C in sealed original container).
Good compatibility with acrylic emulsions, cellulose derivatives, and common water-based crosslinkers (e.g., aziridine or carbodiimide types).
Low surface tension enabling superior substrate wetting on low-energy surfaces such as polyolefins and PET films.
High-performance water-based leather finishing topcoats for footwear and furniture.
Flexible packaging coatings for laminated paper, BOPP, and metallized films.
Textile coating binders for waterproof/breathable functional fabrics.
Wood coating base resin in water-based varnishes and UV-curable hybrid systems.
Adhesive modifiers enhancing toughness and peel strength in water-based laminating adhesives.
| Chemical Type | Anionic aliphatic polyester-based polyurethane dispersion |
| Product Form | Opaque white to light yellow liquid |
| Appearance | Homogeneous, slightly viscous dispersion |
| Solids Content (wt%) | 30.0 ± 1.0% |
| pH (at 25°C) | 7.8 – 8.5 |
| Viscosity (mPa·s, Brookfield LVT, #2 spindle, 60 rpm) | 500 – 1,200 |
| Particle Size (D50, nm) | 80 – 120 |
| Minimum Film Formation Temperature (MFFT) | ≤ 15°C |