Mitsui TAFMER™ DF8200 is a high-flow POE with light weight, high elasticity and low temperature resistance, foamable and crosslinkable, suitable for automotive, packaging and sports goods applications.
High melt fluidity with a melt flow index of 18g/10min at 190°C, suitable for high-speed injection molding and extrusion processes, with high molding efficiency to meet large-scale production needs
Light weight, soft and high elasticity, elongation at break of 950%, low specific gravity balances the lightweight design of products, with good recoverability after deformation by external force
Brittleness temperature below -70°C, maintaining excellent impact resistance in a wide temperature range, no embrittlement at low temperature, and strong weather resistance and environmental adaptability for outdoor use
Excellent compatibility with polyolefin substrates, which can improve the flexibility and impact resistance of the substrate after blending, and support foaming and crosslinking modification to expand application scenarios
High transparency and compliance with health and safety standards, excellent optical properties, suitable for food packaging, medical devices and other fields with safety requirements
Automotive lightweight parts such as bumpers and instrument panels, high elasticity, impact resistance and light weight, balancing vehicle protection and weight reduction needs
Low temperature heat-seal films and easy-peel films for food packaging, high transparency and good sealing performance, complying with food contact standards to ensure packaging hygiene and ease of use
Foamed products for sneaker midsoles, high elasticity and light weight, excellent cushioning after foaming, improving the wearing comfort and rebound experience of shoes
Wire and cable insulation layers/sheaths, low temperature resistance and strong environmental adaptability, suitable for complex outdoor wiring scenarios to ensure electrical use safety
Medical device accessories and food hoses, complying with health standards, high elasticity and flexibility, meeting the safety and use requirements of medical and food fields
| Physical Properties | |
| Density | 0.885 g/cm³ (ASTM D1505) |
| Shore A Hardness | 85 (JIS K6253) |
| Thermal Properties | |
| Melting Point | 66 °C (ASTM D2117) |
| Vicat Softening Temperature | 56 °C (ASTM D1525) |
| Brittleness Temperature | <-70 °C (ASTM D748) |
| Melt Flow Properties | |
| Melt Flow Rate (190°C/2.16kg) | 18 g/10 min (ASTM D1238) |
| Melt Flow Rate (230°C/2.16kg) | 34 g/10 min (ASTM D1238) |
| Mechanical Properties | |
| Tensile Strength at Break | 12 MPa (JIS K7113) |
| Elongation at Break | 950 % (JIS K7114) |
| Torsional Stiffness | 9 MPa (Internal Method) |
| Tear Strength (Die C) | 35.6 kN/m (JIS K6252) |
| Flexural Modulus (1% Secant) | 22.8 MPa (JIS K7171) |