Mitsui TAFMER™ DF910 is a high-transparency POE with excellent resilience and low temperature resistance, good processability and compatibility, suitable for optical, high-end packaging and automotive applications.
Excellent optical properties, high transparency and no haze, suitable for molding transparent/translucent products, with impact resistance to meet the stringent requirements of the optical field
Combined with high resilience and flexibility, elongation at break over 800%, good deformation resistance and recoverability, products can quickly recover to their original state after being subjected to external force
Brittleness temperature below -70°C, maintaining stable mechanical properties in a wide temperature range, no embrittlement at low temperature, stable molecular structure with outstanding weather and aging resistance
Moderate melt flow index, good melt fluidity, wide processing window, easy to form by injection molding, extrusion and other processes, which can improve the processing efficiency of production lines
Excellent compatibility with polyolefins such as PP and PE, supporting crosslinking modification, and the heat resistance, mechanical properties and chemical resistance can be further improved after crosslinking
Optical lenses, camera/telescope lens components, high transparency and impact resistance, ensuring optical imaging effect and improving the service durability of components
High-transparency packaging films for food and medicine, high-end packaging materials for cosmetics and electronics, with excellent high-transparency display performance, both protective and weather resistance
Automotive interior parts such as instrument panels and door panels, with high elasticity and soft touch, improving the texture of vehicle interiors and riding comfort
Automotive exterior parts such as bumpers and body trim strips, low temperature resistance and impact resistance, suitable for complex outdoor environments, ensuring the use stability of components
Polyolefin blend modification, blending with PP/PE can improve the transparency and resilience of the substrate, expanding the application scenarios of transparent elastic products
| Physical Properties | |
| Density | 0.885 g/cm³ (ASTM D1505) |
| Shore A Hardness | 87 (ASTM D2240) |
| Thermal Properties | |
| Melting Point | 66 °C (Internal Method) |
| Brittleness Temperature | <-70 °C (ASTM D746) |
| Vicat Softening Temperature | 63 °C (ASTM D1525) |
| Melt Flow Properties | |
| Melt Flow Rate (190°C/2.16kg) | 1.2 g/10 min (ASTM D1238) |
| Melt Flow Rate (230°C/2.16kg) | 2.2 g/10 min (ASTM D1238) |
| Mechanical Properties | |
| Tensile Strength | >27 MPa (ASTM D638) |
| Elongation at Break | >800 % (ASTM D638) |
| Tear Strength (Die C) | 39.2 kN/m (ASTM D624) |
| Flexural Modulus (1% Secant) | 26.8 MPa (ASTM D790) |
| Tensile Set | 13 % (Internal Method) |