Dow INFUSE™ 9507 is a high-performance olefin block copolymer with excellent flow characteristics, suitable for a wide range of general-purpose thermoplastic elastomer applications including injection molding and profile extrusion. It delivers outstanding haptics in overmolding with PP and PE, while its low density helps control resin and production costs and reduce end-product weight. The talc-dusted surface reduces pellet blocking, making it a preferred choice for balancing performance and process efficiency.
Excellent flow properties: High melt index enables high-speed injection molding and extrusion, improving production efficiency.
Superior high-temperature performance: Maintains elasticity and mechanical properties at elevated service temperatures for harsh conditions.
High elastic recovery: Quick rebound after stress with minimal permanent deformation during long-term use.
Premium overmolding haptics: Provides a smooth, comfortable tactile experience when overmolded onto PP/PE substrates.
Enhanced processability: Talc-dusted surface reduces pellet blocking, with short equipment setup times.
Strong compliance: Meets EU 10/2011 and U.S. FDA FCN 424 food contact standards.
Injection molded products: Automotive interior components and home appliance elastic parts, with shorter cycle times and reduced weight.
PP/PE overmolding: Tool handles, appliance knobs and other overmolded parts for enhanced user comfort.
Profile extrusion: Industrial elastic profiles and seals, ensuring stable performance in high-temperature environments.
High-elastic buffers: Shock-absorbing components for electronic devices and medical equipment, maintaining performance under long-term compression.
| Property | Nominal Value (SI / English) |
|---|---|
| Physical | |
| Density | 0.866 g/cm³ |
| Melt Index (190°C/2.16 kg) | 5.0 g/10 min |
| Mechanical (Compression Molded) | |
| Tensile Modulus - 100% Secant | 1.49 MPa / 216 psi |
| Tensile Strength (Break) | 2.89 MPa / 419 psi |
| Elastomer Properties | |
| Tensile Strength (Break) | 7.00 MPa / 1020 psi |
| Tensile Elongation (Break) | 1900 % |
| Tear Strength | 22.0 kN/m / 126 lbf/in |
| Compression Set (21°C) | 22 % |
| Compression Set (70°C) | 70 % |
| Hardness | |
| Durometer Hardness, Shore A (Compression Molded) | 60 |
| Thermal | |
| Melting Temperature (DSC) | 119 °C / 246 °F |
| TMA (1.00 mm) | 77 °C / 171 °F |
| Additives | |
| Antiblock | No |
| Slip | No |
| Processing Aid | No |
| Surface Treatment | Talc dusted |
| Compliance | |
| EU Regulation | EU 10/2011 |
| FDA Compliance | FCN 424 |