ENGAGE 8411 Polyolefin Elastomer is an ethylene-octene elastomer. It excels in durable injection-molded industrial and consumer goods, as well as compression-molded gaskets, offering high clarity, low density, and good impact properties when blended with PP and PE.
Available in pellet form for easy processing.
High clarity enables visual inspection; low density helps cut costs and reduce product weight.
Improves impact resistance in PP and PE blends, making it suitable for high-melt-flow modifier applications.
Complies with EU and U.S. FDA regulations.
Used in the production of automotive thermoplastic olefins (TPO).
Applied in the injection molding of industrial and consumer goods.
Ideal for the manufacturing of compression-molded gaskets.
Density | 0.880 g/cm³ |
Melt Index (190°C/2.16 kg) | 18 g/10 min |
Mooney Viscosity (ML 1+4, 250°F (121°C)) | 3 MU |
Tensile Modulus - 100% Secant (Compression Molded) | 479 psi / 3.30 MPa |
Tensile Strength (Break, Compression Molded) | 1060 psi / 7.30 MPa |
Tensile Elongation (Break, Compression Molded) | 1000 % |
Flexural Modulus (1% Secant, Compression Molded) | 2830 psi / 19.5 MPa |
Flexural Modulus (2% Secant, Compression Molded) | 2970 psi / 20.5 MPa |
Tear Strength | 271 lbf/in / 47.5 kN/m |
Durometer Hardness (Shore A, 1 sec, Compression Molded) | 81 |
Durometer Hardness (Shore D, 1 sec, Compression Molded) | 27 |
Glass Transition Temperature | - 58.0 °F / - 50.0 °C |
Vicat Softening Temperature | 113 °F / 45.0 °C |
Peak Crystallization Temperature (DSC) | 129 °F / 54.0 °C |