Dow ENGAGE 8150 Toughening Agent

ENGAGE 8150 Polyolefin Elastomer is an ethylene-octene copolymer. It features excellent flow characteristics, delivers superb impact performance in PP/PE blends, is suitable for TPO applications requiring low-temperature impact, and offers good filler loading capacity and cure capabilities.

Features Of Dow ENGAGE 8150 Toughening Agent

  1. Pellet form for convenient processing.

  2. Exhibits excellent flow characteristics and improves impact resistance in PP/PE blends.

  3. Allows high filler loading and can be cured via peroxide, silane, or irradiation.

  4. Offers exceptional heat aging resistance, compression set performance, and weather resistance when cured.

Typical Applications Of Dow ENGAGE 8150 Toughening Agent

  1. Used in general-purpose thermoplastic elastomer production.

  2. Applied for impact modification in polymer blends.

  3. Suitable for thermoplastic olefins (TPO) applications.

  4. Ideal for wire and cable manufacturing, especially for electrical insulation.

Specifications Of Dow ENGAGE 8150 Toughening Agent

Density
0.868 g/cm³
Melt Index (190°C/2.16 kg)
0.50 g/10 min
Mooney Viscosity (ML 1+4, 250°F (121°C))
33 MU
Tensile Modulus - 100% Secant (Compression Molded)
377 psi / 2.60 MPa
Tensile Strength (Break, Compression Molded)
1380 psi / 9.50 MPa
Tensile Elongation (Break, Compression Molded)
810 %
Flexural Modulus (1% Secant, Compression Molded)
2200 psi / 15.2 MPa
Flexural Modulus (2% Secant, Compression Molded)
2090 psi / 14.4 MPa
Tear Strength
213 lbf/in / 37.3 kN/m
Durometer Hardness (Shore A, 1 sec, Compression Molded)
70
Durometer Hardness (Shore D, 1 sec, Compression Molded)
20
Glass Transition Temperature
- 61.6 °F / - 52.0 °C
Vicat Softening Temperature
115 °F / 46.0 °C
Melting Temperature (DSC)
131 °F / 55.0 °C
Peak Crystallization Temperature (DSC)
108 °F / 42.0 °C