INFUSE 9817 is a high-performance olefin block copolymer. It excels in durable, flexible injection-molded industrial and consumer products. With a higher setup temperature for faster molding cycles, plus a high crystallization temperature and low density to reduce costs, it boosts production efficiency.
High upper service temperature ensures stability in varied use environments.
Highly flexible with good elastic recovery, resulting in resilient end-products.
Enables faster injection molding cycles via a higher setup temperature.
Low density reduces part weight, lowering production costs.
Used in the injection molding of industrial goods such as durable mechanical components.
Applied for consumer products requiring flexibility, such as flexible household items.
Density | 0.877 g/cm³ (ASTM D792) |
Melt Index (190°C/2.16 kg) | 15 g/10 min (ASTM D1238) |
Tensile Strength (Break, Compression Molded) | 7.00 MPa (ASTM D638) |
Tensile Modulus - 100% Secant (Compression Molded) | 2.31 MPa (ASTM D638) |
Melting Temperature (DSC) | 248 °F (Dow Method) |
Compliance | EU, No 10/2011; U.S. FDA FCN 424 |
Tear Strength | 177 lbf/in |
Compression Set (70°F (21°C)) | 15 % |
Compression Set (158°F (70°C)) | 58 % |
Durometer Hardness (Shore A, Compression Molded) | 71 |
TMA (39.4 mil (1.00 mm)) | 203 °F |