ENGAGE 7467 is a high-performance ethylene-butene copolymer. It provides superior impact properties for demanding TPO applications, featuring a pellet form, very low density, and compliance with relevant regulations.
Pellet form for easy processing.
Delivers superior impact performance for TPO uses.
Boasts very low density, reducing end-product weight.
Complies with U.S. FDA and EU regulations.
Used in polymer modification to enhance material properties.
Applied in demanding TPO applications requiring high impact performance.
Density | 0.862 g/cm³ |
Melt Index (190°C/2.16 kg) | 1.2 g/10 min |
Mooney Viscosity (ML 1+4, 250°F (121°C)) | 19 MU |
Tensile Modulus - 100% Secant (Compression Molded) | 203 psi / 1.40 MPa |
Tensile Strength (Break, Compression Molded) | 290 psi / 2.00 MPa |
Tensile Elongation (Break, Compression Molded) | 600 % |
Flexural Modulus (1% Secant, Compression Molded) | 595 psi / 4.10 MPa |
Flexural Modulus (2% Secant, Compression Molded) | 580 psi / 4.00 MPa |
Tear Strength | 123 lbf/in / 21.6 kN/m |
Durometer Hardness (Shore A, 1 sec, Compression Molded) | 52 |
Glass Transition Temperature | - 72.4 °F / - 58.0 °C |
Melting Temperature (DSC) | 93.2 °F / 34.0 °C |
Peak Crystallization Temperature (DSC) | 55.4 °F / 13.0 °C |