LG Chem LC565 Impact Modifier

LG Chem LC565 is a general-grade POE prepared with octene comonomer, with core advantages of excellent low temperature resistance (-54℃), good impact resistance and flexibility. Its melt fluidity is suitable for injection molding, and it can effectively improve the low temperature toughness and impact resistance of substrates to meet the general modification and molding needs of multiple fields.

Features Of LG Chem LC565 Impact Modifier

  1. General-grade copolymer system: Prepared with octene comonomer, designed with general formula, suitable for basic modification and molding needs in multiple fields

  2. Excellent low temperature resistance: Glass transition temperature as low as -54℃, stable flexibility and mechanical properties in low temperature environment without embrittlement risk

  3. Good impact resistance and flexibility: Shore A54 low hardness characteristic, excellent impact resistance and good flexibility, which can effectively improve the crack resistance of substrates

  4. Suitable processability: MFR 5.0g/10min, Mooney Viscosity 8MU, good melt fluidity, optimized for injection molding with high molding efficiency

Typical Applications Of LG Chem LC565 Impact Modifier

  1. Automotive Field: Modification of automotive interior and exterior parts (bumpers, fenders, interior parts), improving the low temperature impact resistance and flexibility of components to ensure durability under complex working conditions

  2. Wires & Cables: Insulation and sheathing materials for cables, providing excellent low temperature flexibility and insulation, suitable for wiring needs in low temperature environments

  3. Shoe Manufacturing: Core raw material for shoe soles, endowing soles with high elasticity and soft foot feel, improving wearing comfort and sole folding resistance

Specifications Of LG Chem LC565 Impact Modifier


Physical Properties
Density0.865 g/cm³
Shore A Hardness54 (ASTM D2240)
Melt Flow & Viscosity
Melt Flow Rate (190°C/2.16kg)5.0 g/10 min (ASTM D1238)
Mooney Viscosity (ML 1+4@121℃)8 MU (ASTM D1646)
Mechanical Properties
Tensile Strength at Break1.80 MPa (ASTM D638)
Elongation at Break550 % (ASTM D638)
Flexural Modulus (1% Secant)8.00 MPa (ASTM D790)
Tear Strength20.0 kN/m (ASTM D624)