Dow INFUSE™ 9807 is a high-performance olefin block copolymer designed for durable, flexible injection molded industrial and consumer goods. It features a higher set temperature for faster injection cycle times, while its high crystallization temperature and low density drive lower production costs and reduced part weight. The talc-dusted surface reduces pellet blocking, making it an ideal choice for balancing efficiency and performance.
High flow & rapid molding: High melt index and set temperature enable high-speed injection molding, significantly reducing cycle times.
Superior high-temperature performance: Maintains elasticity and mechanical properties at elevated service temperatures for harsh conditions.
High elastic recovery: Quick rebound after stress with minimal permanent deformation during long-term use.
Cost & weight optimization: High crystallization temperature and low density reduce production costs and part weight.
Enhanced processability: Talc-dusted surface reduces pellet blocking, with short equipment setup times.
Strong compliance: Meets EU 10/2011 and U.S. FDA FCN 424 food contact standards.
Durable injection molded products: Industrial components and consumer durables such as tool handles and elastic parts for appliance housings.
Lightweight structural parts: Automotive interior components and electronic device housings, balancing strength and weight reduction.
High-elastic buffers: Shock-absorbing components for medical devices and sports equipment, maintaining performance under long-term compression.
Composite elastic formulations: Blended with other OBCs to create functional parts with customized hardness and elasticity.
| Property | Nominal Value (SI / English) |
|---|---|
| Physical | |
| Density | 0.866 g/cm³ |
| Melt Index (190°C/2.16 kg) | 15 g/10 min |
| Mechanical (Compression Molded) | |
| Tensile Modulus - 100% Secant | 1.30 MPa / 189 psi |
| Tensile Strength (Break) | 1.21 MPa / 176 psi |
| Tensile Elongation (Break) | 1200 % |
| Elastomer Properties | |
| Tensile Strength (Break) | 3.00 MPa / 435 psi |
| Tensile Elongation (Break) | 2200 % |
| Tear Strength | 17.0 kN/m / 97.1 lbf/in |
| Compression Set (21°C) | 16 % |
| Compression Set (70°C) | 76 % |
| Hardness | |
| Durometer Hardness, Shore A (Compression Molded) | 55 |
| Thermal | |
| Melting Temperature (DSC) | 118 °C / 244 °F |
| TMA (1.00 mm) | 60 °C / 140 °F |
| Additives | |
| Antiblock | No |
| Slip | No |
| Processing Aid | No |
| Surface Treatment | Talc dusted |
| Compliance | |
| EU Regulation | EU 10/2011 |
| FDA Compliance | FCN 424 |