ENGAGE 8440G Polyolefin Elastomer is an ethylene-octene copolymer. It stands out in thermoplastic elastomer applications, serving as an excellent option for blending and compounding, and is available in pellet form for convenient processing.
Pellet form enables easy handling during production.
Performs well across a wide range of thermoplastic elastomer applications.
Contains no antiblock, slip, or processing aid additives.
Boasts good mechanical properties such as tensile strength and elongation.
Utilized in thermoplastic elastomer manufacturing.
Ideal for blending processes in polymer compounding.
Density | 0.897 g/cm³ |
Melt Index (190°C/2.16 kg) | 1.6 g/10 min |
Mooney Viscosity (ML 1+4, 250°F (121°C)) | 13 MU |
Tensile Modulus - 100% Secant (Compression Molded) | 914 psi / 6.30 MPa |
Tensile Strength (Break, Compression Molded) | 2960 psi / 20.4 MPa |
Tensile Elongation (Break, Compression Molded) | 690 % |
Tear Strength | 451 lbf/in / 78.9 kN/m |
Durometer Hardness (Shore A, 1 sec, Compression Molded) | 86 |
Durometer Hardness (Shore D, 1 sec, Compression Molded) | 36 |
Glass Transition Temperature | - 27.4 °F / - 33.0 °C |
Vicat Softening Temperature | 167 °F / 75.0 °C |
Melting Temperature (DSC) | 199 °F / 93.0 °C |
Peak Crystallization Temperature (DSC) | 169 °F / 76.0 °C |