ENGAGE 8200 Polyolefin Elastomer is an ethylene-octene copolymer. It features excellent flow characteristics, performs well in general-purpose thermoplastic elastomer applications, and offers superb impact properties in PP/PE blends, along with high filler loading capacity and good electrical properties.
Pellet form for easy processing.
Exhibits excellent flow characteristics and high filler loading capability.
Provides improved impact resistance in PP and PE blends and excellent electrical properties.
Offers exceptional heat aging resistance, compression set performance, and weather resistance when cross-linked.
Used in general-purpose thermoplastic elastomer production.
Applied for impact modification in polymer blends.
Suitable for wire and cable manufacturing, leveraging its good electrical properties.
Density | 0.870 g/cm³ |
Melt Index (190°C/2.16 kg) | 5.0 g/10 min |
Mooney Viscosity (ML 1+4, 250°F (121°C)) | 8 MU |
Tensile Modulus - 100% Secant (Compression Molded) | 334 psi / 2.30 MPa |
Tensile Strength (Break, Compression Molded) | 827 psi / 5.70 MPa |
Tensile Elongation (Break, Compression Molded) | 1100 % |
Flexural Modulus (1% Secant, Compression Molded) | 1580 psi / 10.9 MPa |
Durometer Hardness (Shore A, 1 sec, Compression Molded) | 66 |
Durometer Hardness (Shore D, 1 sec, Compression Molded) | 17 |
Glass Transition Temperature | - 63.4 °F / - 53.0 °C |
Vicat Softening Temperature | 98.6 °F / 37.0 °C |
Melting Temperature (DSC) | 138 °F / 59.0 °C |
Peak Crystallization Temperature (DSC) | 111 °F / 44.0 °C |