Dow INFUSE 9007 Toughening Agent

INFUSE 9007 is a lower-density, high-performance olefin block copolymer designed for TPE applications requiring elevated service temperatures. It excels in compounds and blends, offering fast processability, high filler loading capacity, and excellent elastic recovery—making it ideal for durable, flexible end-products.

Features Of Dow INFUSE 9007  Toughening Agent

  1. High-Temp Durability: Maintains stable performance in TPE applications with elevated service temperature demands.

  2. Formulation Freedom: Compatible with compounds and blends, and supports high filler loading to achieve customized material properties.

  3. Efficient Processing: Fast setup times and talc-dusted pellets streamline production processes, contributing to cost-effective manufacturing.

Typical Applications Of Dow INFUSE 9007  Toughening Agent

  1. High-Temp TPE Systems: Used in automotive, industrial, or consumer goods that require long-term performance at elevated temperatures.

  2. Compounds & Blends: Enhances formulations with high filler loading and compatibility, enabling custom material solutions.

Specifications Of Dow INFUSE 9007  Toughening Agent

Temperature Performance
High upper service temperature to meet demanding TPE application needs.
Flexibility & Recovery
Highly flexible with good elastic recovery for resilient products.
Processing Efficiency
Fast setup times and talc-dusted pellet form for smooth manufacturing.
Formulation Versatility
General-purpose elastomer excellent for compounds and blends.
Regulatory Compliance
Meets EU (No 10/2011) and U.S. FDA (FCN 424) standards
Density
0.866 g/cm³
Melt Index (190°C/2.16kg)
1.0 g/10 min
Tensile Modulus (100% Secant)
1.61 MPa
Tensile Strength (Break)
5.10 MPa
Elongation at Break
600 %
Tear Strength
27.0 kN/m
Compression Set (70°F)
16 %