ENGAGE 7270 Polyolefin Elastomer is a general-purpose copolymer. It is designed to strike a good cost/performance balance in polymer modification applications, helping enhance properties of base polymers efficiently.
Form & Ease of Use: Available in pellet form, easy to integrate into polymer modification processes.
Cost-Performance Balance: Delivers reliable performance in polymer modification without excessive cost, optimizing value.
Polymer Modification: Used to improve properties (like flexibility, impact resistance) of various polymers in industries such as packaging, automotive, and consumer goods.
Melt Index (190°C/2.16 kg) | 0.80 g/10 min |
Mooney Viscosity (ML 1+4, 250°F (121°C)) | 24 MU |
Tensile Modulus - 100% Secant (Compression Molded) | 537 psi |
Tensile Strength (Break, Compression Molded) | 2020 psi |
Tensile Elongation (Break, Compression Molded) | 720 % |
Flexural Modulus (1% Secant : Compression Molded) | 3260 psi |
Flexural Modulus (2% Secant : Compression Molded) | 3210 psi |
Tear Strength | 302 lbf/in |
Shore Hardness A (1 sec, Compression Molded) | 80 |
Shore Hardness D (1 sec, Compression Molded) | 26 |
Glass Transition Temperature | -47.2 °F |
Vicat Softening Temperature | 122 °F |
Melting Temperature (DSC) | 147 °F |
Peak Crystallization Temperature (DSC) | 122 °F |